Composite crucible and method of manufacturing the same

ABSTRACT

The purpose of the present invention is to provide a crucible which has high viscosity at high temperature, can be used for a long time, and can be manufactured at low cost, and a method of manufacturing the crucible. The present invention provides a composite crucible including a vitreous silica crucible body having a sidewall portion and a bottom portion, and a reinforcement layer provided on an outer surface side of an upper end portion of the vitreous silica crucible body, wherein the reinforcement layer is made of mullite material whose main component is alumina and silica.

CROSS-REFERENCE TO RELATED APPLICATION

This application is related to Japanese Patent Application No.2010-293567 filed on Dec. 28, 2010, whose priority is claimed and thedisclosure of which is incorporated by reference in its entirety.

BACKGROUND OF THE INVENTION

1. Field of the Invention

The present invention relates to a composite crucible used formanufacturing a silicon crystal, and a method of manufacturing thecrucible.

2. Description of the Related Art

Nowadays, the demand for a solar cell has been increasing inconsideration of environment problem and energy problem. The solar cellis generally classified into a silicon solar cell and a compoundsemiconductor solar cell, based on the kind of the semiconductor usedfor the power generation part. Furthermore, the silicon solar cell isclassified into a crystalline silicon solar cell and an amorphoussilicon solar cell. The crystalline silicon solar cell is classifiedinto a monocrystalline silicon solar cell and a polycrystalline siliconsolar cell.

Regarding conversion efficiency which is the most important aspect for asolar cell, nowadays, the compound semiconductor solar cell has reachednearly 25%, which is the highest, and the monocrystalline silicon solarcell is about 20%, and the polycrystalline silicon solar cell and theamorphous silicon solar cell are 5 to 15%. Regarding the raw materialcost, silicon is an element which is the second most abundant on theearth (oxygen is the most abundant), and thus much cheaper than compoundsemiconductor, and thus silicon solar cell is most widely used. Theconversion efficiency refers to a ratio of the energy converted toelectrical energy by the solar cell with respect to the energy of theincoming light into the solar cell. The ratio is represented by“percentage (%)”.

Next, a method of manufacturing a monocrystalline silicon solar cellwill be explained briefly. First, a cylindrical silicon single crystalingot is manufactured by the Czochralski method (the CZ method) or thefloating zone melting method (the FZ method). For example, in the CZmethod, polycrystalline silicon is supplied into a vitreous silicacrucible, followed by melting by heating. Then, a seed crystal is dippedinto the obtained silicon melt, and gradually pulled up, to produce asilicon single crystal.

Then, the ingot is sliced to obtain thin wafers each having a thicknessof, for example, 300 μm. The surface of the obtained wafer is etched bya chemical to remove processing strain in the surface, to obtain a wafer(substrate) for a solar cell. An Impurity (dopant) is diffused into thewafer to form a PN junction on one side of the wafer, and thenelectrodes are formed on both sides, and thereafter an antireflectionfilm is formed on the sunlight incidence plane to reduce light energyloss due to light reflection, to obtain the solar cell. In the solarcell, in order to increase the current, it is important to manufacture asolar cell having a larger area. The CZ method is excellent in that itallows easy production of a silicon single crystal having a largediameter, and the obtained single crystal is excellent in the strength.Therefore, this method is preferred as a method of obtaining a siliconwafer, having a large diameter, which is a substrate material formanufacturing a large-area solar cell.

On the other hand, in the manufacturing of the polycrystalline siliconsolar cell, it is preferred to use the casting method where silicon meltis solidified in the mold, or the electromagnetic casting method whichis a continuous casting method by electromagnetic induction. By use ofsuch method, it is possible to manufacture a substrate material at lowercost than single crystal silicon substrate, which is manufactured by theCZ method. In the casting method, high-purity silicon is heated andmelted in a crucible, and a small amount of boron (which is a dopant)and the like is uniformly added thereto, and the silicon melt issolidified therein or solidified after the silicon melt is introducedinto a mold. It is required that the crucible and the mold used for thecasting method are excellent in heat resistance and shape stability, andin addition low impurity content is also demanded. So, the crucible ismade of silica, and the mold is made of graphite.

The vitreous silica crucible used for manufacturing a silicon crystal isrequired to have high viscosity at high temperature in order to bedurable enough for long-time and multiple pulling or casting.Furthermore, the vitreous silica crucible is required to be manufacturedat low cost. As a conventional crucible having high strength at hightemperature, there are known a crucible having a layer containingaluminium (Al) in high concentration at the outer surface side, acrucible obtained by coating a crystallization promoter (e.g. barium(Ba)) on the outer surface, and a crucible having, on the outer surface,a stabilization layer made of alumina, mullite, or the like (SeeJP-A-2000-247778, JP-A-2008-507467, and JP-A-2004-531449). Anotherrelated reference is JP-A-H1-153579.

SUMMARY OF THE INVENTION

The conventional crucible having the layer containing aluminium (Al) inhigh concentration has relatively high viscosity, but the hightemperature strength is not sufficient. Furthermore, the crucibleobtained by coating barium, as a crystallization promoter, onto asurface can be strengthen by the crystallization of the cruciblesurface, but the coating requires time and effort, and the handling ofthe toxic barium is problematic. Furthermore, in the conventionalcrucible having the stabilization layer on the outer surface, thestabilization layer is formed in a thickness of about 1 mm by thethermal spraying method, and further improvement in strength has beendemanded.

Therefore, the purpose of the present invention is to provide a cruciblewhich has high viscosity at high temperature, can be used for a longtime, and can be manufactured at low cost, and there is also provided amethod of manufacturing the crucible.

The present inventors have made extensive research on the aforementionedproblem, and found out that it is possible to improve the durability ofa crucible by providing a mullite reinforcement layer at the upper endportion of a vitreous silica crucible. When a vitreous silica crucibleis used for a long time, inward sagging of the sidewall of the cruciblecan occur. However, when the reinforcement layer is provided on theupper end portion, such inward sagging can be prevented. Furthermore,there might be an idea of forming the whole or a large portion of thecrucible by use of mullite material. When a vitreous silica layer isprovided on the inner surface, the difference in the thermal expansioncoefficient between mullite and vitreous silica can cause formation ofcracks in the crucible during heating the crucible. However, when thereinforcement layer is formed only on the rim upper end portion, nocracks are formed in the crucible, and thus long-time use is madepossible.

The present invention has been made based on such technical findings,and provides a composite crucible comprising a vitreous silica cruciblebody having a sidewall portion and a bottom portion, and a reinforcementlayer provided on an outer surface side of an upper end portion of thevitreous silica crucible body, wherein the reinforcement layer is madeof mullite material whose main component is alumina and silica.

According to the present invention, the mullite reinforcement layer isprovided on the upper end portion of the vitreous silica crucible body,and thus high temperature strength of the upper end potion of thecrucible can be improved. Therefore, the crucible strength can bemaintained, and long-time use of the crucible is made possible.Furthermore, a large portion of the crucible is made of vitreous silica,and thus the composite crucible can be handled in the same way as theconventional vitreous silica crucible, and thus the handling is easy.

In the present invention, the height of the reinforcement layer ispreferred to be 1/10 to ½ of the height of the sidewall portion. Whenthe height of the reinforcement layer is less than 1/10 of the sidewallportion, the reinforcement layer does not work sufficiently and thusinward sagging of the sidewall portion can occur. When the height of thereinforcement layer is larger than ½ of the height of the sidewallportion, the difference in the thermal expansion coefficients betweenmullite and vitreous silica can cause formation of cracks in thecrucible during heating the crucible.

In the present invention, it is preferred that the composite cruciblefurther comprises a buffer layer between the reinforcement layer and thevitreous silica crucible body, and the buffer layer having concentrationgradient of aluminium concentration which decreases from the above tothe below of the crucible. According to this configuration, the mullitereinforcement layer and vitreous silica can be sufficiently stronglyunited vertically.

In the present invention, the vitreous silica crucible body is preferredto have an opaque vitreous silica layer, provided on the outer surfaceside of the crucible, containing numerous microbubbles and a transparentvitreous silica layer provided on the inner surface side of thecrucible. The opaque vitreous silica layer enhances heat keeping effectof the crucible, and thus enables uniform heating of silicon melt. Thetransparent vitreous silica layer improves the manufacturing yield of asilicon single crystal.

In the present invention, the reinforcement layer may be provided on thesame layer as the opaque vitreous silica layer with respect to the wallthickness direction of the crucible. Alternatively, the reinforcementlayer may be provided on the outer side of the opaque vitreous silicalayer in a way that the reinforcement layer contacts the outer surfaceof the opaque vitreous silica layer. In either case, the vitreous silicacrucible body can be reinforced, and thus there can be provided acrucible which is not readily deformed even after long-time

In the present invention, the concentration of the aluminium containedin the reinforcement layer is preferred to have concentration gradientwhich decreases from the outer surface side toward the inner surfaceside of the crucible. According to this configuration, the viscosity ofthe crucible on the outer surface side is sufficiently high, and thethermal expansion coefficient at a region near the inner surface isclose to that to vitreous silica, and thus they are strongly united. Inaddition, impurity contamination of silicon melt in the crucible can beprevented.

Furthermore, the present invention provides a method of manufacturing acomposite crucible comprising:

a process of, while rotating a mold having a cavity corresponding to ashape of a composite crucible, supplying mullite material powdercontaining alumina powder and silica powder to an upper region of themold, and supplying second silica powder to a lower region providedbelow the upper region;

a process of supplying third silica powder on an inner surface side of alayer made of the mullite material powder and the second silica powder;

a process of heating and fusing the mullite material powder, the secondsilica powder, and the third silica powder to form an opaque vitreoussilica layer provided on the outer surface of the crucible, atransparent vitreous silica layer provided on an inner surface side ofthe crucible, and a mullite reinforcement layer provided on the outersurface side of the crucible upper end portion.

Furthermore, the present invention provides a method of manufacturing acomposite crucible comprising:

a process of forming a vitreous silica crucible body having a sidewallportion and a bottom portion;

a process of forming a mullite ring-shaped reinforcement member obtainedby sintering a composition whose main component is alumina and silica;

a process of joining the reinforcement member on an outer surface sideof the upper end portion of the vitreous silica crucible body.

Thus, according to the present invention, there is provided a cruciblewhich has high strength at high temperature, can be used for a longtime, and can be manufactured at low cost, and there is also provided amethod of manufacturing the crucible.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 is a sectional view schematically showing the structure of acomposite crucible 10 according to a first embodiment of the presentinvention.

FIG. 2 is a graph showing Al concentration distribution with respect tothe thickness direction of a reinforcement layer 14.

FIG. 3 is a flowchart for schematically explaining an exemplary methodof manufacturing a composite crucible 10.

FIGS. 4( a) to (c) are sectional views for schematically explaining anexemplary method of manufacturing a composite crucible 10.

FIG. 5 is a sectional view schematically showing the structure of acomposite crucible 20 according to a second embodiment of the presentinvention.

FIG. 6 is a sectional view schematically showing the structure of acomposite crucible 30 according to a third embodiment of the presentinvention.

FIG. 7 is a flowchart for schematically explaining an exemplary methodof manufacturing the composite crucible 30.

DESCRIPTION OF THE PREFERRED EMBODIMENTS

Hereinafter, with reference to the attached drawings, preferredembodiments of the present invention will be explained.

FIG. 1 is a schematic sectional view showing the structure of acomposite crucible according to a first embodiment of the presentinvention.

As shown in FIG. 1, the composite crucible 10 includes a sidewallportion 11A and a bottom portion 11B, and has a basic shape as acontainer for keeping silicon melt therein. The sidewall portion 11A isa cylindrical portion parallel to the crucible central axis (Z axis).The bottom portion 11B is a relatively flat portion including a point ofintersection with the crucible central axis. There is a corner portion11C between the bottom portion 11B and the sidewall portion 11A. Thecorner portion 11C is a portion where the diameter in the sidewallportion 11A gradually decreases. The wall thickness of the crucible canvary depending on the portion in the crucible, but is preferred to be 5mm or more. Usually, the thickness of mid-size or large-size crucibleswhose opening diameter is 16 inches (approx. 400 mm) or more is 5 mm ormore. Such crucible is preferably used for long time manufacturing, andthus the technical effect by the present invention is eminent in suchcrucible.

In one aspect of the present invention, the composite crucible 10 of thepresent embodiment includes a vitreous silica crucible as basicstructure and mullite (e.g. 3Al₂O₃.2SiO₂) is used for a reinforcementmember for the crucible.

Thus, the composite crucible 10 includes a vitreous silica crucible body11 for keeping silicon melt therein, and a mullite reinforcement layer14 provided on an upper end portion of the vitreous silica crucible body11. A “composite crucible” means that the material for the crucible isnot only vitreous silica as in a conventional crucible, but the materialfor the crucible is mullite and vitreous silica, thus composite. Thename of “composite crucible” should not limit the scope of the presentinvention.

The vitreous silica crucible body 11 includes an opaque vitreous silicalayer 12 provided on the outer side of the crucible, and a transparentvitreous silica layer 13 provided on the inner surface side of thecrucible. As illustrated, the opaque vitreous silica layer 12 and thereinforcement layer 14 constitutes a crucible outer layer, and thetransparent vitreous silica layer 13 constitutes a crucible inner layercovering the inner surface of the opaque vitreous silica layer 12 andthe reinforcement layer 14.

The opaque vitreous silica layer 12 is amorphous vitreous silica layerincorporating numerous microbubbles. In the present specification,“opaque” refers to a state that numerous microbubbles exist in vitreoussilica and the vitreous silica appears opaque. The opaque vitreoussilica layer 12 has a function of uniformly conveying, to silicon meltin the crucible, heat from a heater disposed around the crucible. Theopaque vitreous silica layer 12 has larger heat capacity than thetransparent vitreous silica layer 13, and thus enables easy control ofthe temperature of silicon melt.

The bubble content rate of the opaque vitreous silica layer 12 is higherthan the transparent vitreous silica layer 13, and is not in particularlimited as long as it exerts the function, but is preferred to be 0.7%or more. When the bubble content rate of the opaque vitreous silicalayer 12 is less than 0.7%, the opaque vitreous silica layer 12 does notproperly function. The bubble content rate of the opaque vitreous silicalayer 12 can be calculated from the specific gravity. An opaque vitreoussilica piece having an unit volume (1 cm³) is cut out from the crucible.When the mass is A, and the specific gravity for vitreous silica notcontaining bubbles is assumed to be B=2.21 g/cm³, the bubble contentrate is P (%)=(A/B)*100.

The transparent vitreous silica layer 13 is an amorphous vitreous silicalayer substantially not containing bubbles. The transparent vitreoussilica layer 13 prevents the increase of vitreous silica pieces detachedfrom the crucible inner surface, and thus enhances silicon singlecrystallization yield. Here, “substantially not containing bubbles”refer to a state that the bubble content rate and the bubble size aresuch that the single crystallization yield is not deteriorated due tothe bubbles. Although not in particular limited, it is preferred thatthe bubble content rate is 0.1% or less and the average diameter of thebubbles is 100 μm or less. The bubble content rate of the transparentvitreous silica layer can be measured nondestructively by use of anoptical detection unit. As the optical detection unit, a light-receivinglens and an image pickup unit can be employed. In order to measure thebubble content rate from the surface to a certain depth, the focus ofthe light-receiving lens is scanned from the surface to the depth. Theobtained image data is processed in an image processing device tocalculate the bubble content rate.

The change of the bubble content rates from the opaque vitreous silicalayer 12 to the transparent vitreous silica layer 13 is relativelyabrupt. At a position approx. 30 μm from a position where the bubblecontent rate of the transparent vitreous silica layer 13 starts toincrease, the bubble content rate reaches that of the opaque vitreoussilica layer 12. Therefore, the boarder between the opaque vitreoussilica layer 12 and the transparent vitreous silica layer 13 is clearand can be easily visually distinguished.

The transparent vitreous silica layer 13 may be made of natural vitreoussilica or synthetic vitreous silica. Natural vitreous silica is vitreoussilica manufactured from natural silica such as silica stone, naturalquartz crystal. In general, natural silica contains metal impurities inhigher concentration and OH group in lower concentration than syntheticsilica. For example, for natural silica, the Al content is 1 ppm ormore, and the content of each element of alkali metals (Na, K and Li) is0.05 ppm or more, and the OH group content is less than 60 ppm. Naturalsilica has larger viscosity at high temperature than synthetic silica,and thus enhances the high temperature strength of the whole crucible.In addition, natural silica is cheaper than synthetic silica, and thusthe use of natural silica is advantageous in terms of cost.

On the other hand, synthetic vitreous silica is vitreous silicamanufactured from synthetic silica obtained, for example, by hydrolysisof silicon alkoxide. In general, synthetic silica contains metalimpurities in lower concentration and OH group in higher concentrationthan natural silica. For example, for synthetic silica, the content ofeach element of metal impurities is less than 0.05 ppm, and the OH groupcontent is 30 ppm or more. However, synthetic silica containing metalimpurities such as Al is also known. Thus, whether silica is natural orsynthetic needs to be determined based on plural factors. Syntheticvitreous silica contains impurities in much lower concentration thannatural vitreous silica, and thus prevents the increase of impuritiesreleased into silicon melt from the crucible, and thus enhances siliconsingle crystallization yield.

The transparent vitreous silica layer 13 is preferred to contain each ofalkali metals (Na, K and Li) in an amount of 0.05 ppm or less. This isbecause, when the crucible body 11 contains a large amount of alkalimetals, the amount of impurities released into silicon melt from thecrucible can increase, and the quality of silicon single crystal candeteriorate. A crucible used for pulling a silicon ingot forsemiconductor devices needs to meet with the aforementioned conditions.However, a crucible used for pulling a single crystal for a solar cellmay contain a relatively large amount of alkali metals.

The thickness of the transparent vitreous silica layer 13 is preferredto be 0.5 mm or more. When the transparent vitreous silica layer 13 isthinner than 0.5 mm, the transparent vitreous silica layer 13 can betotally corroded during pulling a silicon single crystal, and thus thecrucible body 11 can be exposed. The thickness of the transparentvitreous silica layer 13 does not have to be constant from the sidewallportion 11A to the bottom portion 11B, and for example, the thickness ofthe transparent vitreous silica layer 13 can be thicker at the cornerportion 11C than the sidewall portion 11A and bottom portion 11B.

The reinforcement layer 14 is provided on the outer surface side of theupper end portion of the composite crucible 10. The reinforcement layer14 is made of mullite material whose main component is alumina andsilica. The reinforcement layer 14 is provided from the rim upper end toa point 5 to 10 cm below the rim upper end of the crucible.

Mullite is a material containing silicon dioxide (SiO₂) and aluminumoxide (Al₂O₃) in a predetermined ratio. Mullite is white and opaquematerial, and the melting point can vary dependent on the ratio of SiO₂and Al₂O₃, but is approx. 1850 deg. C. Thus, mullite has larger strengthat high temperature than vitreous silica. Mullite has larger viscosityat high temperature than vitreous silica. Thus, by use of mullite, thestrength at high temperature of the overall crucible can be enhanced.Furthermore, mullite is cheaper than vitreous silica, and thus the useof mullite is advantageous in terms of cost.

The thermal expansion coefficient of mullite can vary dependent on theratio of SiO₂ and Al₂O₃, but is known as 4.3 to 4.9 (10⁻⁶K⁻¹). Incontrast, the thermal expansion coefficient of Al₂O₃ is 7.8 and thethermal expansion coefficient of vitreous silica is 0.56. Although thethermal expansion coefficient of mullite is larger than vitreous silica,they can be readily combined. Therefore, it is possible to preventdetachment, due to difference in the thermal expansion coefficient, ofthe reinforcement layer 14 from the vitreous silica crucible body 11 byproperly controlling the temperature during heating and cooling.However, in view of the aforementioned difference in the thermalexpansion coefficient, the area of their interface is preferred to be assmall as possible, and thus the reinforcement layer 14 is provided onlyon the rim upper end portion, not on the whole crucible.

The height H₁ of the reinforcement layer 14 is preferred to be 0.1 H₂ ormore and 0.5 H₂ or less with respect to the height H₂ of the sidewallportion 11A of the crucible. When the height H₁ of the reinforcementlayer 14 is 0.1 H₂ or less with respect to the height H₂ of the sidewallportion 11A of the crucible, the reinforcement layer 14 cannot properlyexert the function, and thus there can occur inward sagging of thesidewall portion.

On the other hand, the crucible is accommodated in a graphite susceptor,the outer surface of the bottom portion 11B and the corner portion 11Cof the crucible is supported by the graphite susceptor. Furthermore, theinner surface of the bottom portion 11B and the corner portion 11C ofthe crucible contacts silicon melt for a long time, and receives theweight of the silicon melt, and thus the bottom portion 11B and thecorner portion 11C is unlikely to be deformed. Thus, reinforcement ofthe bottom portion 11B and the corner portion 11C is not very muchnecessary. In contrast, when the height H₁ of the reinforcement layer 14is larger than 0.5 H₂, heat stress is applied to the crucible, duringheating the crucible, due to the difference of the thermal expansioncoefficients of mullite and vitreous silica, and thus cracks can beeasily formed in the sidewall portion. Furthermore, aluminium containedin mullite is an impurity for a silicon crystal, and thus the use ofmullite needs to be minimized. For these reasons, the height H₁ of thereinforcement layer 14 is preferred to be 0.5 H₂ or less.

FIG. 2 is a graph showing Al concentration change with respect to thethickness direction of the reinforcement layer 14.

As shown in FIG. 2, Al concentration contained in the mullitereinforcement layer 14 may have concentration gradient which lowers fromthe outer surface toward the inner surface. When the reinforcement layer14 is thus configured, the thermal expansion coefficient of thereinforcement layer 14 near the crucible inner surface side of thecrucible body 11 becomes closer to that of vitreous silica, and thusdetachment therebetween due to difference of the thermal expansioncoefficients can be prevented. Thus, the bonding therebetween can beenhanced. Furthermore, when the Al concentration on the inner surfaceside of the crucible is low and thus the contamination, by Al, of thesilicon melt within the crucible can be prevented.

According to the composite crucible 10 of the present embodiment, areinforcement member made of mullite is used to reinforce the cruciblebody 11 made of vitreous silica, and thus the composite crucible 10 hasbetter durability at high temperature than a conventional vitreoussilica crucible. Therefore, the use of the composite crucible 10 enablesmulti-pulling where plural silicon single crystals are pulled from asingle crucible by re-charging silicon material, and thus drasticallyreduces the production cost for silicon single crystals. Furthermore,most portion of the composite crucible 10 is made of vitreous silica,and thus the composite crucible 10 can be handled in the same way as theconventional vitreous silica crucible, and thus it is not necessary tolargely change the temperature control conditions during pulling asilicon single crystal.

The composite crucible 10 having the mullite reinforcement layer 14 onthe upper end portion of the crucible contains impurities (Al) in ahigher concentration than a crucible made of only vitreous silica, andthus the composite crucible 10 is not necessarily appropriate forpulling a silicon single crystal for semiconductor devices. However, thecrucible inner surface contacting silicon melt is covered with atransparent vitreous silica layer, and thus the release of impurities issuppressed to some extent. Therefore, the composite crucible 10 isappropriate for pulling a silicon single crystal for use having largetolerance in terms of impurities, such as for use in a solar cell.Furthermore, mullite is cheaper than silica material, and thus the useof mullite is advantageous in terms of cost. Therefore, the use ofmullite enables production of silicon wafer at lower cost.

Next, with reference to FIGS. 3 and 4, the method of manufacturing thecomposite crucible 10 will be explained.

FIG. 3 is a flowchart for schematically explaining a method ofmanufacturing the composite crucible 10. FIGS. 4( a) to (c) aresectional views for schematically explaining a method of manufacturingthe composite crucible 10. The composite crucible 10 can be manufacturedby use of the rotating mold method. In the rotating mold method, asshown in FIG. 4( a), a carbon mold having a cavity coinciding with theouter shape of the crucible is used to supply crucible material powdertherein while rotating the mold, to form a material powder layer alongthe inner surface of the mold. In this process, the mullite materialpowder 16 a is supplied on the cavity upper region corresponding to theupper end portion of the crucible, and silica powder (second silicapowder) 15 b is supplied on a region lower than the upper region. Inparticular, silica powder 15 b is first supplied (Step S11), andthereafter mullite material powder 15 a is supplied (Step S12). Thecarbon mold 16 is rotated at a constant speed, and thus a centrifugalforce is applied to the supplied material powder to maintain the shapeon the inner surface.

Mullite material powder 15 a is material powder obtained by mixingalumina powder and silica powder (first silica powder), for example, inthe ratio of 3:2 in element ratio. When the Al concentration in thereinforcement layer is desired to be changed in the thickness directionof the crucible as shown in FIG. 2, plural kinds of mullite materialpowder different in the ratio of alumina powder and silica powder may beprepared and supplied into the mold. As the silica powder 15 b, naturalsilica powder is preferred to be used.

Next, as shown in FIG. 4( b), silica powder 15 c (third silica powder)which is the material of the transparent vitreous silica layer 13 issupplied in the mold 16 having a layer of mullite material powder 15 aand silica powder 15 b which are the material for the opaque vitreoussilica layer 12, to increase the thickness of the silica powder layer(Step S13). Silica powder 15 c is supplied into the mold so as to form alayer with a certain thickness. Silica powder 15 c may be natural silicapowder or synthetic silica powder.

Thereafter, as shown in FIG. 4( c), arc electrodes 17 are disposed inthe cavity to heat the inside of the mold to 1720 deg. C. or more to arcfuse the material powder (Step S14). Furthermore, during the heating,the silica powder layer is depressurized via ventilation holes providedin the mold, to remove bubbles in the crucible inner surface and thus toform a transparent vitreous silica layer 13. Thereafter, thedepressurization is weakened or terminated during heating to leavebubbles in the silica powder layer, to form an opaque vitreous silicalayer containing numerous microbubbles. In this process, numerousmicrobubbles stays in the reinforcement layer 14, too. Thereafter, therim of the crucible was cut off so that the upper end of the cruciblebecomes flat (Step S15). Thus, the composite crucible 10 according tothe present embodiment is manufactured.

Thus, according to the method of manufacturing a composite crucible ofthe present embodiment, the mullite reinforcement layer is formedtogether with the silica powder layer by arc fusing, and thus ahigh-quality crucible having high durability at high temperature can bemanufactured efficiently while maintaining the quality of a conventionalvitreous silica crucible.

Next, the composite crucible according to the second embodiment of thepresent invention will be explained in detail.

FIG. 5 is a sectional view schematically showing the structure of thecomposite crucible according to a second embodiment of the presentinvention.

As shown in FIG. 5, the composite crucible 20 of the present embodimentis characterized in that a buffer layer 18 is provided between theopaque vitreous silica layer 12 and the reinforcement layer 14 disposedabove the opaque vitreous silica layer 12. The buffer layer 18 is alayer in which the Al concentration of the mullite reinforcement layer14 gradually decreases from the above to the below. The buffer layer 18has concentration gradient in the vertical direction, which is incontrast to the concentration gradient in the thickness direction of thecase shown in FIG. 2. According to this configuration, the difference ofthe thermal expansion coefficients between the opaque vitreous silicalayer 12 and the mullite reinforcement layer 14 is reduced, and thuscracks caused by heat stress in the interface therebetween can beprevented.

FIG. 6 is a schematic sectional view showing the structure of acomposite crucible according to a third embodiment of the presentinvention.

As shown in FIG. 6, the composite crucible 30 of the present embodimentis characterized in that the mullite reinforcement layer 14 is providedon the outer side of the vitreous silica crucible body 11. Therefore,the reinforcement layer 14 is in contact with the outer surface of theopaque vitreous silica layer 12 which constitutes the outer layer of thevitreous silica crucible body 11. The reinforcement layer 14 is providedby preparing a ring-shaped member separately from the vitreous silicacrucible body 11, and joining the ring-shaped member with the outersurface of the vitreous silica crucible for integration. Otherconfiguration is substantially the same the composite crucible 10 of thefirst embodiment, and thus the same references are assigned to the samecomponents, and the explanation is not repeated.

FIG. 7 is a flowchart for explaining a method of manufacturing thecomposite crucible 30.

As shown in FIG. 7, in manufacturing the composite crucible 30, thevitreous silica crucible body 11 is first prepared (Step S21). Thevitreous silica crucible body 11 can be prepared by the aforementionedrotating mold method. Unlike the first embodiment, the opaque vitreoussilica layer 12 is formed up to the rim upper end, but otherconfiguration is substantially identical.

Next, a mullite ring-shaped reinforcement member, which will be thereinforcement layer 14, is prepared (Step S22). The mullitereinforcement member can be prepared, for example, by the slip castingmethod. The slip casting method is well known as a method of forming aceramic sintered body. Usually, a mold made of a material having goodwater absorbability such as plaster is used. Slurry (suspension ofceramic powder, also referred to as “slip”) is injected into a cavity inthe mold, and water in the slurry is absorbed to solidify the slurry.The obtained molded body is subjected to a degreasing process, andthereafter fired to obtain the final product. The method is, in general,appropriate for manufacturing a molded body having a complex shape, buttakes long time to manufacture a molded body having a large wallthickness. Thus, also known is the compression molding technique inwhich the slip casting molding method is carried out while pressure isapplied to slurry. According to the slip casting compression moldingmethod, slurry is forcedly dewatered, and thus a molded body having arelatively thick wall can be manufactured.

When the ring-shaped reinforcement member is molded by use of the slipcasting method, slurry is first prepared by dispersing, in water,alumina powder and silica powder (material for mullite) in a certainratio, and thereafter the slurry is further dispersed after acrystallization promoter is added thereto. Furthermore, the slurry issupplied into a mold and dewatered to obtain a molded body whose maincomponent is alumina and silica. In the present embodiment, it ispreferred that the mold is attached to a rotating axis, and is rotatedto forcedly dewater the slurry. Next, the molded body solidified by thedewatering is dried for a certain period, and subjected to a degreasingprocess, and thereafter fired at 1400 deg. C., to obtain the mullitereinforcement member.

Next, the ring-shaped reinforcement member is attached on the outer sideof the rim upper end portion of the vitreous silica crucible body 11 tojoin them (Step S23). Thus, the reinforcement layer 14 is formed on theouter side of the vitreous silica crucible body 11. Thereafter, thevitreous silica crucible body 11 and the reinforcement layer 14 aretogether subjected to the rim cutting process so that the upper end ofthe crucible is flat (Step 24). It is possible to obtain a flat upperend by adjusting the height position of the reinforcement layer withrespect to the vitreous silica crucible body 11. However, the heightadjustment is difficult, and thus it is better to obtain the flat upperend by rim cutting them together. Thus, the composite crucible 30 of thepresent embodiment is obtained.

The present invention is not in particular limited, and can be modifiedas long as the modification does not depart from the spirits of thepresent invention, and the modification is incorporated in the presentinvention.

EXAMPLE Example 1

Sample A1 of the composite crucible was prepared. The crucible had adiameter of 16 inches (opening diameter of about 400 mm), a height ofthe 250 mm. The wall thickness of the crucible was 6.5 mm at thestraight body portion, 8 mm at the corner portion, and 5 mm at thebottom portion. The thicknesses of the transparent vitreous silica layerand the opaque vitreous silica layer at the sidewall portion were 0.5 mmand 6 mm, respectively. Furthermore, a mullite reinforcement layer wasprovided on the upper end portion of the crucible. The height H₂ of thesidewall portion was 150 mm and the height H₁ of the reinforcement layerwas about 15 mm (H₁=0.1 H₂).

Next, Crucible Sample A1 was heated for a long time in a furnace, andthe deformation state of the crucible was observed. The heatingconditions were as follows. First the temperature was increased at aconstant rate from the room temperature to about 1580 deg. C. over 5hours, and the temperature was maintained at 1580 deg. C. for 25 hours.Thereafter, the temperature was decreased to 1500 deg. C., and thetemperature was maintained at 1500 deg. C. for 100 hours. Thereafter,the temperature was decreased at a constant rate to the room temperatureover 7 hours.

The heating test was carried out in a state that no silicon material wasin the crucible. In a normal use of the crucible, silicon material issupplied in the crucible, and thus the crucible wall is pressed from theinside by silicon melt. When no silicon material is in the crucible,inward sagging of the sidewall portion of the crucible is more likely tooccur. This state is similar to the state after most portion of siliconmelt in the crucible is consumed by pulling a silicon single crystal.The result of the heating test is shown in Table 1.

As shown in Table 1, deformation such as inward sagging and buckling wasnot visually observed in the aforementioned heating test in CrucibleSample A1 having the mullite reinforcement layer having a height of 15mm formed on the outer surface side of the crucible upper end portion.In addition, there was no crack on the sidewall portion.

Example 2

Crucible Sample A2 having the same structure except that the height H₁of the reinforcement layer was about 50 mm (H₁≈0.33 H₂) was prepared andsubjected to the same heating test as in Example 1. As shown in Table 1,deformation such as inward sagging and buckling was not visuallyobserved, and there was no crack on the sidewall portion.

Example 3

Crucible Sample A3 having the same structure except that the height H₁of the reinforcement layer was about 75 mm (H₁=0.5 H₂) was prepared andsubjected to the same heating test as in Example 1. As shown in Table 1,deformation such as inward sagging and buckling was not visuallyobserved, and there was no crack on the sidewall portion.

Example 4

Crucible Sample A4 having the same structure except that the height H₁of the reinforcement layer was about 100 mm (H₁≈0.67 H₂) was preparedand subjected to the same heating test as in Example 1. As shown inTable 1, deformation such as inward sagging and buckling was notvisually observed, but there were many cracks on the sidewall portion.

Example 5

Crucible Sample A5 having the same structure except that the height H₁of the reinforcement layer was about 10 mm (H₁≈0.067 H₂) was preparedand subjected to the same heating test as in Example 1. As shown inTable 1, inward sagging and buckling occurred slightly.

Example 6

Crucible Sample A6 having the same structure except that the height H₁of the reinforcement layer was about 100 mm (H₁≈0.67H₂) was prepared andsubjected to the same heating test as in Example 1. As shown in Table 1,deformation such as inward sagging and buckling was not visuallyobserved, and there was no crack on the sidewall portion.

Comparative Example 1

Sample B1 of a conventional vitreous silica crucible was prepared. Thecrucible had a transparent vitreous silica layer on the inner surfaceside, and an opaque vitreous silica layer on the outer surface side. Thecrucible had a diameter of 16 inches (opening diameter about 400 mm), aheight of the 250 mm. The wall thickness of the crucible was 6.5 mm atthe straight body portion, 8 mm at the corner portion, and 5 mm at thebottom portion. The thicknesses of the transparent vitreous silica layerand the opaque vitreous silica layer at the sidewall portion were 0.5 mmand 6 mm, respectively. Sample B1 was subjected to the same heating testas in Example 1. The result is shown in Table 1.

As shown in Table 1, in Sample B1 which is a conventional vitreoussilica crucible, inward sagging and buckling occurred after long-timeheating, and the roundness largely deteriorated.

TABLE 1 Height of Height of Ratio of Buff- Cruci- Sidewall Reinforce-Height er ble Portion ment Layer H₁/H₂ Layer State of Sample H₂ (mm) H₁(mm) (mm) (mm) Heating Ex. 1 (A1) 150 15 0.1 None No Deformation NoCrack Ex. 2 (A2) 150 50 0.33 None No Deformation No Crack Ex. 3 (A3) 15075 0.5 None No Deformation No Crack Ex. 4 (A4) 150 100 0.67 None NoDeformation Many Crack Ex. 5 (A5) 150 10 0.067 None Slight DeformationEx. 6 (A6) 150 100 0.67 25 No Deformation No Crack Comp. 150 0 0 NoneLarge Ex. 1 (B1) Deformation

EXPLANATION OF REFERENCE SYMBOL

-   10 Composite Crucible-   11 Vitreous Silica Crucible Body-   11A Sidewall Portion-   11B Bottom Portion-   11C Corner Portion-   12 Opaque Vitreous Silica Layer-   13 Transparent Vitreous Silica Layer-   14 Reinforcement Layer-   15 a Mullite Material Powder-   15 b Silica Powder (Second Silica Powder)-   15 c Silica Powder (Third Silica Powder)-   16 Carbon Mold-   17 Arc Electrodes-   18 Buffer Layer-   20 Composite Crucible

1. A composite crucible comprising: a vitreous silica crucible bodyhaving a sidewall portion and a bottom portion, and a reinforcementlayer provided on an outer surface side of an upper end portion of thevitreous silica crucible body, wherein the reinforcement layer is madeof mullite material whose main component is alumina and silica.
 2. Thecomposite crucible of claim 1, wherein the height of the reinforcementlayer is 1/10 to ½ of the height of the sidewall portion.
 3. Thecomposite crucible of claim 1, further comprising a buffer layer betweenthe reinforcement layer and the vitreous silica crucible body, and thebuffer layer having concentration gradient of aluminium concentrationwhich decreases from the above to the below of the crucible.
 4. Thecomposite crucible of claim 1, wherein the vitreous silica crucible bodyhas an opaque vitreous silica layer, provided on an outer surface sideof the crucible, containing numerous microbubbles and a transparentvitreous silica layer provided on an inner surface side of the crucible.5. The composite crucible of claim 4, wherein the reinforcement layer isprovided on the same layer as the opaque vitreous silica layer withrespect to the wall thickness direction of the crucible.
 6. Thecomposite crucible of claim 4, wherein the reinforcement layer isprovided on the outer side of the opaque vitreous silica layer in a waythat the reinforcement layer contacts the outer surface of the opaquevitreous silica layer.
 7. A method of manufacturing a composite crucibleof claim 1 comprising: a process of, while rotating a mold having acavity corresponding to a shape of a composite crucible, supplyingmullite material powder obtained by mixing alumina powder and silicapowder to an upper region of the mold, and supplying second silicapowder to a lower region provided below the upper region; a process ofsupplying third silica powder on an inner surface side of a layer madeof the mullite material powder and the second silica powder; a processof heating and fusing the mullite material powder, the second silicapowder, and the third silica powder to form an opaque vitreous silicalayer provided on the outer surface of the crucible, a transparentvitreous silica layer provided on an inner surface side of the crucible,and a mullite reinforcement layer provided on the outer surface side ofan upper end portion of the crucible.
 8. A method of manufacturing acomposite crucible of claim 1 comprising: a process of forming avitreous silica crucible body, for supporting silicon melt, having asidewall portion and a bottom portion; a process of forming a mullitering-shaped reinforcement member obtained by sintering a compositionwhose main component is alumina and silica; a process of joining thereinforcement member on an outer surface side of an upper end portion ofthe vitreous silica crucible body.